Development of a Geopolymer for 3D Printing Using Submerged Arc Welding (SAW) Slag

Reducing the carbon footprint of the construction sector is a growing priority. This study explores the potential of using submerged arc welding (SAW) slag as a precursor in the development of low-carbon geopolymeric materials for 3D printing. The influence of potassium hydroxide (KOH) molarity, partial replacement of ground granulated blast furnace slag (GGBFS) with SAW slag, and water-to-binder (w/b) ratio was evaluated in terms of fresh and hardened properties. Increasing KOH molarity delayed setting times, with the longest delays at 10 M and 12 M. The highest compressive strength (48.5 MPa at 28 days) was achieved at 8 M; higher molarities led to strength losses due to excessive precursor dissolution and increased porosity. GGBFS replacement increased setting times due to its higher Al2O3 and MgO content, which slowed geopolymerization. The optimized formulation, containing 20% SAW slag and activated with 8 M KOH at a w/b ratio of 0.29, exhibited good workability, extrudability, and shape retention. This mixture also performed best in 3D printing trials, strong layer adhesion and no segregation, although minor edge irregularities were observed. These results suggest that SAW slag is a promising sustainable material showing for 3D-printed geopolymers, with further optimization of printing parameters needed to enhance surface quality.