Symmetric two-electodes pseudosupercapacitor from trichalcogenide MoS₃-MoO₃-poly-O-amino-benzenethiol nanocomposite

A novel nanocomposite, MoS 3 -MoO 3 /poly-O-amino-benzenethiol (MoS 3 -MoO 3 /POABT), has been synthesized in a one-pot process and demonstrates promising applications as a material for a two-electrode configuration supercapacitor. This nanocomposite exhibits remarkable morphological characteristics, featuring uniform particles with an average diameter of 80 nm and a porous structure. The advantageous morphology contributes to the enhanced performance of the fabricated pseudo supercapacitor. The evaluation of the charge/discharge behavior and cyclic voltammetry curves of the redox reaction of the MoS 3 -MoO 3 /POABT nanocomposite reveals its efficacy as a supercapacitor material. The specific capacitance (CS) achieved for this fabricated supercapacitor is noteworthy at 152 F/g. Furthermore, the energy density (E) peaks at 12.6 W h kg −1 when operating at a current density of 0.2 A/g. This high energy density demonstrates the supercapacitor’s ability to store significant energy for practical use efficiently. Importantly, its stability remains strong, with an impressive 98% retention after 250 cycles, and even after 1000 cycles, it only slightly decreases to 95%. This remarkable stability over extended cycling periods underscores the durability of the materials in the supercapacitor. Such reliable performance establishes the MoS 3 -MoO 3 /POABT nanocomposite as a dependable choice for supercapacitor applications, ensuring longevity and consistent performance in diverse energy storage needs.