Exploring the Use of Fe2.5Ni2.5Sn3 as a Monolithic Catalyst for Oxygen Evolution Reaction Under Alkaline Conditions

Enabling a hydrogen fuel-based economy is reliant on the discovery of materials that catalyze the electrolysis of water which requires low-cost catalytic electrodes to improve the kinetics of the oxygen evolution reaction. Fe2.5Ni2.5Sn3, was prepared by arc-melting and electrochemical studies were conducted to evaluate its ability to catalyze the oxygen evolution reaction. Potentiodynamic polarization testing revealed that the Fe2.5Ni2.5Sn3 alloy had a Tafel slope of 48 mV/decade and required an overpotential of 326 mV in order to obtain a current density of 10 mA/cm2. X-ray photoelectron spectroscopy studies indicated that the native oxide present on the surface became hydrated upon subjecting it to oxygen evolution studies.