Preparation and Properties of Polyaniline/Hydroxypropyl Methylcellulose Composite Conductive Thin Films

In this work, a chemical grafting polymerization method was employed to synthesize EHPMC-g-PANI self-supporting films. Polyaniline (PANI) was grafted onto hydroxypropyl methylcellulose (HPMC) modified with epichlorohydrin (EPHMC) to obtain an EHPMC-g-PANI aqueous dispersion, which was subsequently dried to form the self-supporting films. The introduction of HPMC, with its excellent film-forming ability and mechanical strength, successfully addressed the poor film-forming ability and mechanical properties intrinsic to PANI. Compared to in situ polymerized HPMC/PANI, the EHPMC-g-PANI exhibited significantly improved storage stability. Moreover, the fabricated EHPMC-g-PANI films displayed a more uniform and smoother morphology. The conductivity of all the films ranged from 10−2 to 10−1 S/cm, and their tensile strength reached up to 36.1 MPa. These results demonstrate that the prepared EHPMC-g-PANI holds promising potential for applications in various fields, including conductive paper, sensors, and conductive inks.