Effect of annealing process on microstructure, residual stress, and fatigue behaviour of AISI 2205 duplex stainless steel

This study investigated the microstructure, residual stress, and fatigue behavior of duplex stainless steels that have been annealed with different annealing processes. A cold-rolled AISI 2205 Duplex Stainless Steel (DSS) sample was annealed in three ways for this purpose. In modes 1 and 2, samples were annealed at 500°C for 6 and 8 hours, respectively. The sample was annealed for 6 hours at 950°C for mode 3.The Optical Microscopy (OM) technique was used to determine the crystallographic texture and microstructural characteristics. An X-ray Diffraction (XRD) analysis was used to determine the residual stresses in austenite and ferrite phases on pre- and post-heat-treated samples. The Scanning Electron Microscope (SEM) technique was utilized to assess fatigue cracks. The results showed that the texture microstructure of the specimens using mode 1 and 2 were remained; the grain had a smaller fragmentation. The elongation grains of the specimen after mode 3 were smaller, relatively spheroidal, and more homogeneous. There was a reduction in residual stress after mode 3 annealing process. The fatigue strength of the specimens that under applied this process was 11.1% higher than that of specimens in the as-received state.