Dual configuration of shallow acceptor levels in 4H-SiC

Acceptor dopants in 4H-SiC exhibit energy levels that are located deeper in the band gap than the thermal energy at room temperature (RT), resulting in incomplete ionization at RT. Therefore, a comprehensive understanding of the defect energetics and how the impurities are introduced into the material is imperative. Herein, we study impurity related defect levels in 4H-SiC epitaxial layers (epi-layers) grown by chemical vapor deposition (CVD) under various conditions using minority carrier transient spectroscopy (MCTS). We find two trap levels assigned to boron impurities, B and D, which are introduced to varying degrees depending on the growth conditions. A second acceptor level that was labeled X in the literature and attributed to impurity related defects is also observed. Importantly, both the B and X levels exhibit fine structure revealed by MCTS measurements. We attribute the fine structure to acceptor impurities at hexagonal and pseudo-cubic lattice sites in 4H-SiC, and tentatively assign the X peak to Al based on experimental findings and density functional theory calculations.