In vitro analysis shows sandblasting enhances shear bond strength and surface roughness in 3D printed and heat-cured acrylic, suggesting improved prosthodontic applications.
Removable dental prostheses remain a reliable treatment for edentulous patients. Conventional fabrication requires multiple steps, whereas computer-aided design and manufacturing (CAD-CAM), particularly 3D printing, offers faster and more cost-effective alternatives. This in vitro study aimed to evaluate the effect of sandblasting on surface roughness and shear bond strength of silicone soft liner bonded to 3D-printed and heat-cured acrylic denture base materials. Eighty specimens were divided into four groups: heat-cured control, 3D-printed control, heat-cured sandblasted, and 3D-printed sandblasted. Surface roughness was measured using a profilometer, while shear bond strength was tested with a universal testing machine. Data were analyzed with one-way ANOVA and Games-Howell post hoc test. Sandblasting significantly increased both surface roughness and shear bond strength compared to untreated groups. The 3D-printed specimens showed higher roughness values after sandblasting than heat-cured ones. Sandblasting improves surface roughness and bonding performance of both heat-cured and 3D-printed denture base resins, supporting its use as an effective surface treatment in prosthodontics.
No takes yet. Share an insight, caveat, or question.
Wadi et al. (2025) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: