Oxidation-Resistant Ni-AlSi12 Composite Coating with Strong Adhesion on Ti-6Al-4V Alloy Substrate via Mechanical Alloying and Subsequent Laser Cladding

Two Ni-AlSi12 coatings were prepared using mechanical alloying (MA) and mechanical alloying followed by laser cladding (LC), respectively. Phase composition and microstructure variations caused by powder weight ratio and laser-specific energy were thoroughly analyzed in this study. Mechanical properties and oxidation behavior are markedly improved by subsequent laser cladding. The MA-LC coating, characterized by high densification and crack-free properties, presents a homogeneous microstructure with refined features. Microhardness testing reveals a marked superiority of the MA-LC coating over the conventional MA coating. The nano-hardness of MA-LC coating is 9.79 GPa, exhibiting that it is 6.84 times the nano-hardness of the MA sample. Owing to metallurgical bonding, the MA-LC coating possesses excellent scratch bonding performance. The MA-LC coating shows favorable oxidation behavior, due to the following three reasons: Firstly, oxygen diffusion can be effectively blocked by the compact Al2O3 oxide layer developed on the MA-LC coating surface, which reduces the oxidation velocity. Secondly, the coating’s mean grain dimensions demonstrate an increasing tendency after oxidation, which reduces the grain boundary serving as the oxygen diffusion channel. This enhancement significantly improves the coating’s oxidation resistance. Thirdly, analysis of the coating’s respective kernel average misorientation (KAM) map revealed a significant release of internal stress following 100 h oxidation, which can improve the coating’s resistance to spallation.