Analysis demonstrates improved corrosion resistance and wear properties in Mo/MoN coatings, indicating their potential for artificial joints.
In this study, Cr/CrN and Mo/MoN alternating multilayer coatings with pure metal interlayers were deposited on 316 L stainless steel substrates via physical vapor deposition to systematically investigate the corrosion resistance, wear resistance, and tribocorrosion behavior of the multilayer coating systems in physiological saline environments. Microstructural characterization revealed that the CrN layer consists of mixed CrN and Cr2N phases, whereas the MoN layer exhibits a highly densified microstructure along with the presence of MoO2 phase, which collectively contribute to the superior corrosion resistance of the Mo/MoN coating. Furthermore, compared to the CrN layer, the MoN layer demonstrates enhanced nanomechanical properties and improved resistance to crack initiation, due to the greater hardness and higher H/E and H3/E2 values. Consequently, the Mo/MoN coating exhibits significantly better wear and tribocorrosion performance than its CrN counterpart. This work provides a theoretical foundation for the design of tribocorrosion-resistant hard coatings for artificial joint materials.
No takes yet. Share an insight, caveat, or question.
Chen et al. (2025) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: