Effect of Welding Current on Microstructure and Mechanical and Corrosion Properties of 7075/7075 Pulsed MIG Welded Joints

This study investigates the effects of welding current on the microstructure, mechanical properties, and corrosion behavior of 7075/7075 pulsed metal inert gas (P-MIG) welded joints. Welding experiments were conducted at currents of 190 A, 200 A, and 210 A using ER5356 filler wire, with the joints analyzed through optical microscopy (OM), scanning electron microscopy (SEM/EDS), and tensile and hardness testing, as well as intergranular and electrochemical corrosion evaluations. The results reveal that increasing welding current alters the solidification dynamics and precipitation behavior in the WZ. At 190 A, refined and uniformly distributed dendrites were obtained, whereas at 210 A, grains coarsened and elemental segregation was more pronounced. The weld hardness exhibited a trend of first increasing and then slightly decreasing with increasing welding current, with a maximum value of 99.5 HV0.1 obtained at 200 A. Similarly, the tensile strength improved with increasing welding current, reaching 257.7 MPa with 8% elongation at 210 A. Corrosion resistance exhibited a non-monotonic trend, with the best performance observed at 200 A, as indicated by the shallowest intergranular corrosion depth, the most positive open-circuit potential, and the highest charge transfer resistance in electrochemical impedance spectroscopy. The findings demonstrate that welding current is a critical parameter controlling the balance between microstructural refinement, mechanical strengthening, and corrosion resistance, and that 200 A represents the optimal condition under the investigated parameters. These insights provide theoretical guidance and experimental evidence for process optimization in the welding of high-strength aluminum alloys.