As an important renewable building material, wood’s flammability significantly limits its application range. This study addresses the environmental pollution issues associated with traditional flame retardants by developing an eco-friendly flame retardant system based on natural biomaterials. Utilizing layer-by-layer self-assembly techniques, sodium phytate, chitosan, sodium alginate, and sodium methyl silicate were sequentially deposited onto the wood surface to construct a multifunctional composite coating. A multifunctional composite coating was constructed on wood surfaces through layer-by-layer self-assembly technology, involving successive deposition of phytic acid sodium, chitosan, sodium alginate, and methyl silicate sodium. Characterization results indicated that the optimized sample WPCSMH achieved a limiting oxygen index of 34.0%, representing a 12% increase compared to untreated wood. Cone calorimetry tests revealed that its peak heat release rate and total heat release were reduced by 57.1% and 25.3%, respectively. Additionally, contact angle measurements confirmed its excellent hydrophobic properties, with an initial contact angle of 111°. Mechanistic analysis reveals that this system significantly enhances flame retardant performance through a synergistic interaction of three mechanisms: gas phase flame retardancy, condensed phase flame retardancy, and free radical scavenging. This research provides a sustainable and innovative pathway for developing environmentally friendly, multifunctional wood-based composites.
Li et al. (Sun,) studied this question.