Study on Stress Corrosion Resistance of Multiphase Composite Nanobainitic Steel via Isothermal Treatment

This study examines the electrochemical behavior and slow strain rate tensile (SSRT) properties of 67Si2CrNiAlMnMoCu steel featuring a multiphase nanobainitic microstructure consisting of bainitic ferrite (BF), retained austenite (RA), and martensite (M). Electrochemical measurements reveal that both the corrosion tendency and dissolution rate decrease with extended austempering time, with the sample austempered at 220 °C for 21 h showing the lowest corrosion susceptibility. SSRT results indicate that specimens with a nearly fully bainitic microstructure exhibit increased strength sensitivity to stress corrosion. Notably, the specimen austempered at 240 °C for 9 h demonstrates excellent corrosion resistance while retaining favorable overall mechanical properties, exhibiting a tensile strength-based stress corrosion cracking sensitivity coefficient as low as 4.1%.