This article is focused on the preparation of barium titanate nanopowder/epoxy composites and studying the effect of barium titanate nanopowder on improving mechanical and thermal characteristics of the epoxy polymer. Composites are prepared by dispersing barium titanate nanopowder in epoxy resin and, subsequently, cross-linking by using diamino diphenyl methane (DDM) curing agents. Synthesis of barium titanate nanopowder/epoxy composites is carried out for different concentrations (1, 3, and 5 by weight) of barium titanate nanopowder at high temperature. High-temperature curing (HTC) involves mixing the resin-nanopowder solution followed by DDM hardener and curing at 120°C. Tensile, flexure, and impact results showed a maximum value of 72.7 MPa, 2.98 GPa, and 2 J/cm, respectively. DSC analysis revealed that curing occurs at low temperature in the presence of barium titanate nanopowder. Thermogravimetry analysis (TGA) showed the increased thermal stability in the nanoparticle filled epoxy composites as compared with the pure epoxy counterparts. Dynamic mechanical analysis (DMA) revealed, maximum storage modulus of 6400 MPa and glass transition temperature of 154°C for 3 wt% barium titanate nanopowder.
No takes yet. Share an insight, caveat, or question.
Chandradass et al. (2008) studied this question.
Synapse has enriched 5 related papers. Consider them for comparative context: