Nuclear magnetic relaxation and molecular motion in poly(vinylidine fluoride)

Pulsed NMR T 1 , T 2 , and T 1ρ measurements are reported for poly(vinylidine fluoride) (PVF 2 ). The results demonstrate clearly the presence of four relaxation processes, three amorphous and one crystalline. The α relaxation is undoubtedly a crystalline one, while β and γ are both amorphous, in agreement with earlier conclusions from dielectric and dynamic mechanical measurements. The fourth relaxation (β′) observed initially in the mechanical measurements of Kakutani, but undetected in dielectric experiments, has been confirmed in our results and the process is described by an activation energy of 15.1 kcl/mole. Motion of folds on the surface of crystal lamellae is deemed to be the responsible mechanism for the β′ relaxation. Two models have been considered in the interpretation of the α process; rotation of crystalline chains in the vicinity of defects and rotational oscillation of restricted amplitude of all crystalline chains about the main chain axes. Rotation of amorphous chains is a possible mechanism for the γ process while motions of a general nature are responsible for the β relaxation. Our experimental results again indicate that spin diffusion plays an important role in the overall NMR response of the polymer.