Epoxy-sized textile-grade polyacrylonitrile (PAN) carbon fiber (TCF) with 450 K filaments (CFTF, ORNL) was reinforced in the polycarbonate (PC) matrix using a compression molding technique. The epoxy sizing effect on the surface, thermal, and mechanical properties of TCF–PC was investigated. X-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy results of the TCF–PC composite show the absence of an oxirane group (epoxy-sized TCF), which suggests a covalent bond formation between the oxirane ring and carbonyl groups from TCF and PC. Dynamic mechanical analysis results confirm a strong immobilized interface (b > 1) present between TCF and PC. The tensile, flexure, compression, and interlaminar shear strength of TCF–PC composites were 323 ± 53, 371 ± 31, 397 ± 87, and 36 ± 3 MPa, correspondingly. The fracture analysis through scanning electron microscopy shows good wettability between TCF and the PC matrix which validates the results obtained from surface and thermal characterization.
No takes yet. Share an insight, caveat, or question.
Kore et al. (2021) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: