The rational design of electrode architectures is essential for advancing high-performance supercapacitors. In this study, Nd2O3 electrodes with controlled structural features were developed via a polyacrylic acid (PAA)-assisted hydrothermal approach. By systematically tuning PAA concentration, the growth mechanism of Nd2O3 was effectively regulated, leading to a distinct morphological transition from compact agglomerates to well-defined hierarchical structures. The optimized Nd2O3-P2 electrode exhibits a porous and interconnected architecture, providing enhanced electrolyte accessibility and shortened ion diffusion pathways. This structural optimization significantly improves electrochemical performance, delivering a high areal capacitance of 26.889 F/cm2 at 10 mA/cm2, along with excellent rate capability and reduced internal resistance. Kinetic analysis reveals that charge storage is predominantly governed by diffusion-controlled Faradaic processes, with the optimized structure facilitating rapid ion transport and efficient redox activity. Additionally, the electrode demonstrates excellent cycling durability, retaining 87.08% capacitance over 12,000 cycles. An asymmetric supercapacitor assembled using Nd2O3-P2 and activated carbon achieves stable operation up to 1.5 V, delivering good capacitance retention (81.2%) after 7000 cycles. This work highlights the effectiveness of PAA-induced structural tuning and provides a practical strategy for developing advanced rare earth oxide-based electrodes for energy storage applications.
Amate et al. (Wed,) studied this question.