Preparation and Thermal Properties of Dense Polycrystalline Oxyhydroxyapatite

Solution‐grown crystals of hydroxyapatite were sintered into polycrystalline oxyhydroxyapatite bodies, using the range 1050 to 1450°C. The heat capacity, thermal diffusivity, and thermal conductivity of the sintered bodies were measured by the laser flash method at 130–1000 K. The sintered bodies were 94.4 to 99.4% of theoretical density and 0.8 to 12 μm in grain size. Sintering is accompanied by grain growth and by vacancy formation and cell contraction due to thermal dehydration. Typical values of the heat capacity, thermal diffusivity, and thermal conductivity at room temperature are 0.73 J/g K, 0.0057 cm 2 /s and 0.013 J/s cm K, respectively. Low‐temperature thermal conductivity increased with increasing temperature, similarly to that of amorphous solids. This odd behavior is discussed in terms of phonon mean free path.