Structure and molecular conformation of tussah silk fibroin films: Effect of heat treatment

Structural changes of tussah (Antheraea pernyi) silk fibroin films induced by heat treatment were studied as a function of the treatment temperature in the range 200–250°C. The DSC curve of tussah films with α-helix molecular conformation displayed characteristic endo and exo peaks at 216 and 226°C, respectively. These peaks first weakened and then completely disappeared after heating at 230°C. Accordingly, the TMA thermal shrinkage at 206°C disappeared when the films were heated at 230°C. The onset of weight loss was monitored at 210°C by means of TG measurements. X-ray diffraction profiles gradually changed from α-helix to β-sheet crystalline structure as the treatment temperature increased from 200 to 250°C. On raising the heating temperature above 200°C, the intensity of IR and Raman bands characteristic of β-sheet conformation increased in the whole ranges of amide and skeletal modes. The sample treated at 200°C showed a spectral pattern intermediate between α-helix and β-sheet molecular conformation. The IR marker band for random coil structure, still detectable at 200°C, disappeared at higher treatment temperatures. Spectral changes attributable to the onset of thermal degradation appeared at 230°C.