Processing and Evaluation of CFRP and GFRP Composites Manufactured by Closed-Injection Pultrusion: Effects of Resin Viscosity and Pulling Speed

Pultrusion is an efficient continuous manufacturing process for fiber-reinforced polymer (FRP) composites, but conventional open-bath impregnation has limitations such as resin exposure, quality variation, and resin loss. To overcome these limitations, closed-injection pultrusion (CIP) and short-pot-life resin systems have recently been introduced. However, the effects of processing variables on the quality and properties of composites manufactured using such resin systems have not been fully clarified. In this study, the effects of resin viscosity and pulling speed on the quality and mechanical properties of carbon FRP (CFRP) and glass FRP (GFRP) composites manufactured by CIP were investigated. CFRP and GFRP composites were fabricated at resin temperatures of 30 and 40 °C and pulling speeds of 300, 400, and 500 mm/min. The manufactured composites were evaluated in terms of void content, microstructure, hardness, and tensile properties. The results showed that increasing pulling speed increased void content and promoted macrovoids and locally poor impregnation, whereas the influence of resin temperature was relatively limited. Hardness, tensile strength, and elastic modulus decreased as pulling speed increased. These results demonstrate that CFRP and GFRP composites can be successfully manufactured by CIP using short-pot-life resin systems, and that precise control of resin viscosity and pulling speed is essential for achieving high quality and mechanical performance.