γ→β Phase transformation induced in poly(vinylidene fluoride) by stretching

The purpose of this work was to show in a conclusive way the γ→β phase transformation induced by uniaxial stretching in poly(vinylidene fluoride). Poly(vinylidene fluoride) films were melted and crystallized at 163°C for 36 h. Under these conditions, a mixture of α and γ phases was formed, with a predominance of the latter. These films were uniaxially stretched at 130°C at a draw ratio of 4. Fourier transform infrared and differential scanning calorimetry analyses showed a γ→β phase transition in the solid state, whereas orientation of the α phase without any transition was observed. Optical microscopy analysis permitted the observation of the transformation of spherulitic structures into oriented lamellae during stretching.