New technique of processing highly oriented poly(vinylidene fluoride) films exclusively in the β phase

Oriented β‐phase films were obtained by utilizing two different techniques: conventional uniaxial drawing at 80 °C of predominantly α‐phase films, and by drawing almost exclusively β‐phase films obtained by crystallization at 60 °C from dimethylformamide (DMF) solution with subsequent pressing. Wide angle X‐ray diffraction (WAXD) and pole figure plots showed that with the conventional drawing technique films oriented at a ratio ( R ) of 5 still contained about 20% of phase α, a crystallinity degree of 40% and β‐phase crystallographic c ‐axis orientation factor of 0.655. Drawing at 90 °C and with R = 4 of originally β‐phase films results in exclusively β‐phase films with crystallinity degree of 45% and orientation factor of 0.885. Crystalline phase, crystallinity degree, and crystallographic c ‐axis orientation factor of both phases were also determined for α‐phase oriented films obtained by drawing α‐phase films at 140 °C. For films drawn at 140 °C the α to β phase transition drops to about 22%. Reduction in crystallinity degree with increasing R is more pronounced at draw temperature of 140 °C compared with 80 °C. Moreover, for both phases the c ‐axis orientation parallel to the draw direction is higher at draw temperature of 140 °C than at 80 °C.