Ternary Phosphides Ba M ₂ P ₂ : Tailoring Crystal and Electronic Structures Enables Highly Efficient HER Electrocatalysis

Binary transition metal phosphides and their solid solutions have emerged as promising hydrogen evolution reaction (HER) catalysts. Although many research endeavors have adopted strategies to vary compositions to optimize catalytic performance, they mainly focus on binary structures, which represent only a small fraction of the abundant phase space of structure types among transition metal phosphides. The largely unexplored class of ternary and multinary ordered phosphides in catalysis comprises two or more metals with quite different chemical nature, concealing the structure–property relationships essential for advancing catalyst design. Here, we explored phosphides crystallizing in one of the most abundant ordered intermetallic structure types, —the ThCr 2 Si 2 type, —where square nets of 3 d transition metal M and P atoms are separated by layers of electropositive Ba cations. Four ternary Ba M 2 P 2 ( M = Fe, Fe/Cu, Fe/Ni, Ni) catalysts were synthesized and characterized. BaNi 2 P 2 showed high HER activity in acidic electrolyte, which required an overpotential, η 10, of only 62 mV to drive current density j = –10 mA/cm 2 and high stability with a potential drop rate of 0.25 mV/h. BaNi 2 P 2 outperformed other Ni-based catalysts, such as Ni 2 P and Ni 5 P 4 . Notably, at current densities above –170 mA/cm 2, BaNi 2 P 2 outperformed the standard Pt electrode measured under identical conditions. Electronic structure analysis revealed a volcano-type activity trend among the four Ba M 2 P 2 catalysts based on their d -band center positions, highlighting the role of electropositive Ba cations in shifting the Ni-3 d orbitals into an optimal position.