In Situ Fabrication of a Superhydrophobic ORMOSIL Coating on Wood by an Ammonia–HMDS Vapor Treatment

A superhydrophobic ORMOSIL (organically modified silicate) coating was in situ fabricated on a wood surface by ammonia–hexamethylisilazane (HMDS) vapor treatment. The wood was immerged in tetraethoxysilane (TEOS), and then the TEOS absorbed on the wood surface was hydrolyzed and condensed to hydrophobic SiO2 nanoparticles with ammonia and HDMS vapor treatment. The effect of the treatment temperature and time on the hydrophobicity of wood was investigated. At a treatment temperature of 50 °C, a superhydrophobic surface was achieved on the wood with a treatment time longer than 2 h. SEM images indicated that there were SiO2 nanoparticles fabricated on the wood surface, and FTIR revealed that the hydrophobic –Si(CH3)3 groups were incorporated on the wood surface. The ORMOSIL-modified wood possessed improved liquid repellency. The water absorption decreased significantly from 72.3% to 31.9% after modification.