Crack initiation and crack propagation under thermal cyclic loading

Theoretical and experimental investigations of crack initiation and crack propagation under thermal cyclic loading are presented. For the experimental investigation a special thermal fatigue test rig has been constructed in which a small circular cylindrical specimen is heated up to a homogeneous temperature and cyclically cooled down under well defined thermal and mechanical boundary conditions by a jet of cold water. At the end of the cooling phase the specimen is reheated to the initial temperature and the following cycle begins. The experiments are performed with uncracked and mechanically precracked specimens of the German austenitic stainless steel X6CrNi 1811.In the crack initiation part of the investigation the number of load cycles to initiate cracks under thermal cyclic load is compared to the number of load cycles to initiate cracks under uniaxial mechanical fatigue loading at the same strain range as in the cyclic thermal experiment. The development of initiated cracks under thermal cyclic load is compared with the development of cracks under uniaxial mechanical cyclic load.In the crack propagation part of the investigation crack growth rates of semi-elliptical surface cracks under thermal cyclic loading are determined and compared to suitable mechanical fatigue tests made on compact-tension and four-point bending specimens with semi-elliptical surface cracks. The effect of environment, frequency, load shape and temperature on the crack growth rate is determined for the material in mechanical fatigue tests.The theoretical investigations are based on the temperature distribution in the specimen, which is calculated using finite element programs and compared to experimental results. From the temperature distribution, elastic and elastic-plastic stress distributions are determined taking into account the temperature dependence of the material properties. The prediction of crack propagation relies on linear-elastic fracture mechanics. Stress intensity factors are calculated with the weight function method and crack propagation is determined using the Paris relation.To demonstrate the quality of the crack growth analysis the experimental results are compared to the prediction of crack propagation under thermal cyclic load.