In this letter, the growth of dense W2C nanowires by a simple thermal annealing of sputter-deposited WCx films in nitrogen ambient is reported. Straight nanowires with a density of 250–260μm−2 and length∕diameter in the range of 0.2–0.3μm∕13–15nm were obtained from the 700°C-annealed samples, which exhibit good electron field emission characteristics with a typical turn-on field of about 1.7V∕μm. The self-catalytic growth of W2C nanowires is attributed to the formation of α-W2C phase caused by carbon depletion in the WCx films during thermal annealing.