Phase transitions in mesophase macromolecules. III. The transitions in poly(ethylene terephthalate‐co‐p‐oxybenzoate)

The glass and melting transitions of poly(ethylene terephthalate‐co‐ p ‐oxybenzoate)s have been studied by differential scanning calorimetry. Despite the higher glass transition expected for polyoxybenzoate, there is almost no change in the glass transition temperature up to 63 mol % oxybenzoate (353 ± 4 K). At high oxybenzoate concentration there seems to be a discontinuous jump to a glass transition of 450 K. This high glass transition has been observed in two‐phase materials down to 30 mol % oxybenzoate. The melting transition shows signs of isodimorphism with a minimum in melting temperature at about 60–70 mol % oxybenzoate, 60 K below the melting temperature of poly(ethylene terephthalate). The thermal properties are little affected by the change of the noncrystalline parts of the molecules to a mesophase structure. The transition to the isotropic phase could not be analyzed because of prior decomposition.