Corrosion Resistance of Sintered Austenitic Stainless Steels in Boiling Nitric Acid

A comparative study of the corrosion resistance in boiling nitric acid has been carried out for P/M and cast AISI 304L and AISI 316L stainless steels. The influence of sensitization and acid concentration on the corrosion rate have been determined. The results are discussed with reference to ASTM A262 (Huey test). Scanning electron microscopy was used to study the microstructural characteristics and the corrosion products. It is shown that the corrosion phenomenon in P/M steels is almost entirely due to pore induced crevices; a possible corrosion mechanism for the materials is proposed. © 1997 Canadian Institue of Mining and Metallugy. Published by Elsevier Science Ltd. All rights reserved Résumé On a entrepris une étude comparative de la résistance à la corrosion dans l'acide nitrique bouillant des aciers inoxydables AISI 304L et AISI 316L produits par P/M (par métallurgie des poudres) et moulés. On a déterminé l'influence de la sensibilisation et de la concentration d'acide sur le taux de corrosion. On discute des résultats en faisant référence à la norme ASTM A 262 (test d'Huey). On a utilisé un microscope à balayage électronique pour étudier les caractéristiques de la microstructure et les produits de corrosion. On montre que le phénomène de corrosion chez les aciers en P/M est presqu'entièrement dû aux fissures amorçees aux pores; on propose un mécanisme possible de la corrosion des matériaux en question.