White light emitting diode by using α-Ca2P2O7:Eu2+, Mn2+ phosphor

The α-Ca2P2O7:Eu2+, Mn2+ phosphors show two emission bands peaking at around 416 (blue) and 600nm (orange), originating from the allowed f-d transition of Eu2+ and the forbidden T14-A16 transition of Mn2+, respectively, under near ultraviolet (UV) excitation at 400nm. Spectroscopy and fluorescence lifetime measurements demonstrate that energy transfer from Eu2+ to Mn2+ performs with transfer efficiency as high as 65% for Mn2+ concentration of 12mol%. The authors have fabricated a white light emitting diode (LED) through the integration of GaN near-UV chip and two phosphor blends (α-Ca2P2O7:Eu2+, Mn2+ blue-orange phosphor and Ba2SiO4:Eu2+ green phosphor) into a single package. The white LED shows color rendering index of 78, luminescent efficiency of 9lm∕W, and low color point variation against forward-bias currents.