Abstract 2‐(6‐Oxido‐6H‐dibenzo〈c,e〉〈1,2〉oxa‐phosphorin‐6‐yl)1,4‐benzenediol (ODOPB) and bis(3‐dihydroxyphenyl) phenyl phosphate (BHPP) were successfully synthesized and used as reactive flame retardants in o ‐cresol formaldehyde novolac epoxy resin. Because of the rigid, cyclic, side‐chain structure of ODOPB, the resultant phosphorus‐containing epoxy resin exhibited a higher glass‐transition temperature, better flame retardancy, higher modulus, and greater thermal stability than the regular bromine‐containing tetrabromobisphenol A epoxy resin and the linear, main‐chain, phosphorus‐containing BHPP epoxy resin. A UL‐94VO rating was achieved with a phosphorus content as low as 1.1% with ODOPB (comparable to a bromine content of 12% and a phosphorus content of 2.2% with BHPP) in the cured resins, and no fumes or toxic gas emissions were observed.