Thermal Behavior Investigation of LiNi1/3Co1/3Mn1/3O₂‐Based Li‐ion Battery under Overcharged Test

Thermal behavior of its components such as separator, electrolyte, cathode, anode, and each binder were investigated by differential scanning calorimetry and thermal gravimetric (DSC/TG) to explain thermal runaway mechanism of Li‐ion battery under overcharged test. DSC results indicated the decomposition reaction temperature of SEI (solid electrolyte interface) layer in anode was at about 126°C. It was found that heat generation in anode under normal charged state increased obviously with the increasing of charged voltage. When the battery was overcharged to 4.6 V or 5.0 V, the onset temperature and heat generation of thermal reaction in anode changed a little, while those in cathode had large increase. It was proposed that thermal behavior in cathode mainly caused by the reaction of electrolyte with evolutional oxygen played a key role to thermal runaway for the studied Li‐ion battery under overcharged test.