We have investigated Ag-indium tin oxide (ITO) scheme for obtaining high-quality p-type ohmic contacts for GaN-based light-emitting diodes (LEDs). The Ag(1 nm)-ITO(200 nm) contacts exhibit greatly improved electrical characteristics when annealed at temperatures in the range 400/spl deg/C-600/spl deg/C for 1 min in air, yielding specific contact resistances of /spl sim/10/sup -4/ /spl Omega//spl middot/cm/sup 2/. In addition, the contacts give transmittance of about 96% at 460 nm, which is far better than that of the conventionally used oxidized Ni-Au contacts. It is shown that the luminous intensity of blue LEDs fabricated with the Ag-ITO contacts is about three times higher than that of LEDs with oxidized Ni-Au contacts. This result strongly indicates that the Ag-ITO scheme can serve as a highly promising p-type ohmic contact for the realization of high brightness near ultraviolet LEDs.
No takes yet. Share an insight, caveat, or question.
Song et al. (2005) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: