High peak power λ∼3.3 and 3.5 μm InGaAs/AlAs(Sb) quantum cascade lasers operating up to 400 K

We demonstrate λ∼3.5 μm and λ∼3.3 μm strain compensated In0.7Ga0.3As/AlAs(Sb)/InP quantum cascade lasers operating in pulse regime at temperatures up to at least 400 K. Peak optical power exceeding 3.5 W at 300 K has been achieved at both wavelengths for 10 μm wide 4 mm long lasers with high reflectivity coated back facets. Threshold current densities of 2.5 kA/cm2 and 3.5 kA/cm2 have been observed at 300 K for the devices emitting at λ∼3.5 μm and λ∼3.3 μm, respectively.