Internal motions in an alternating copolymer of ethylene and tetrafluoroethylene

Internal motions in an alternating copolymer of ethylene and tetrafluoroethylene were investigated by dynamic mechanical and dielectric measurements and by nuclear magnetic resonance. At 1 Hz the α, β, and γ relaxations were observed at 110, −25, and −120°C in a quenched sample. The activation energy was 76 kcal/mole for the α relaxation and 10.6 kcal/mole for the γ relaxation. These relaxations are attributed to the motion of long and short segments in the amorphous regions, respectively. The β relaxation, which was observed only in the dynamic mechanical experiments, appears to occur in the crystalline regions. The copolymer is isomeric with poly(vinylidene fluoride), but it has a higher melting point and a much lower dielectric loss.