The post‐curing of a bisphenol A‐glycidyl‐methacrylate based copolymer system at 37°C and 100 percent relative humidity was monitored using Fourier Transform IR (FT‐IR). The dependence of degree of post‐curing on the monomer and initiator components was investigated. The further polymerization achieved by elevating the temperature was measured using differential scanning calorimetry (DSC). The results clearly demonstrated that this free radical curing process was severely quenched by vitrification. Furthermore, a rapid loss in the reactivity to further curing was observed for the material in the quenched state, and this loss in reactivity was attributed to the decay of free radicals.