Void formation in Nickel during high temperature proton irradiation

Pure Ni foils, doped with He from 0 to 28 appm, were irradiated with protons at temperatures in the range 0.3–0.6 Tm (Tm = melting point in °K) and void formation was studied. The influence of He doping, irradiation temperature and alloying were investigated. For constant He content and proton fluence, void number density and swelling are maximum at about 400°C, while the void size increases with temperature. Most voids are octahedral in shape with no sign of truncation. Helium is required to nucleate voids, and lowering the stacking fault energy by alloying suppresses void formation completely. Present results suggest that void nucleation is inhomogeneous. Some implications of these findings are discussed.