Long‐term atmospheric corrosion rates of hot dip galvanised steel and zinc‐aluminium‐magnesium coated steel

This is the authors' abstract. We don't add key points for this paper.

Zn coated steel (Z) and ZnAlMg coated steel (ZM3.7/3 = Zn–Al (3.7 wt.%)‐Mg (3.0 wt.%)) have been exposed for 6 years at twelve different weathering sites world wide. The mass loss of the coatings have been measured after 1, 2, 4, and 6 years exposure. From the results, it is shown that ZM3.7/3 had always a better corrosion performance compared to Z. The ratio of performance after 6 years of exposure varied from about 1.4 to 4.4 with a mean value of 2.8. At temperate marine sites (e.g., temperature between 9–20°C) with low to moderate SO 2 pollution a good relationship was observed between the relative performance of ZM3.7/3 and the corrosion rate of Z. It was thus concluded that ZM3.7/3 has a better relative performance in harsh environments. The corrosion performance of ZM3.7/3 was shown to be connected to the formation of protective corrosion products.