Viscoelastic properties of epoxy‐diamine networks

Eight epoxy–diamine networks have been formed, diamines with 2 to 12 methylene groups being used as curing agents. Dynamic mechanical tests revealed four transition regions in the dynamic loss modulus/temperature relationship. Two possible explanations for the relaxation of the glycidyl portion of the structure are proposed. One of the relaxations could be due to the breakdown of hydrogen bonds through the hydroxyl and ether groups. The second could be ascribed to the relaxation of the unbonded glycidyl groups or a second relaxation of the glycidyl groups after the breakdown of the hydrogen bonds.