In situ synchrotron based x-ray fluorescence and scattering measurements during atomic layer deposition: Initial growth of HfO2 on Si and Ge substrates

The initial growth of HfO2 was studied by means of synchrotron based in situ x-ray fluorescence (XRF) and grazing incidence small angle x-ray scattering (GISAXS). HfO2 was deposited by atomic layer deposition (ALD) using tetrakis(ethylmethylamino)hafnium and H2O on both oxidized and H-terminated Si and Ge surfaces. XRF quantifies the amount of deposited material during each ALD cycle and shows an inhibition period on H-terminated substrates. No inhibition period is observed on oxidized substrates. The evolution of film roughness was monitored using GISAXS. A correlation is found between the inhibition period and the onset of surface roughness.