Correlations between structure and electrical properties of Cr Ta thin films prepared by oblique angle co-sputtering

This is the authors' abstract. We don't add key points for this paper.

Cr Ta thin films were deposited on glass and (100) silicon substrates by DC magnetron co-sputtering. Films were prepared by the glancing angle deposition (GLAD) method by fixing the deposition angle to 80° for both targets. The Cr and Ta target currents were systematically and reversely changed from 0 mA to 300 mA, so as to tune the composition of the films. All other working parameters were kept constant. For such GLAD co-sputtering conditions, the deposition time was adjusted in order to get a film thickness close to 400 nm. A columnar microstructure was obtained with a Janus-like architecture as a function of the operating target currents. Different morphologies and tilted column angles were produced by adjusting target currents. The typical hexagonal Cr phase was produced for Cr-rich films, whereas a mixture of α and β-Ta phases for Ta-rich films. DC electrical resistivity vs. temperature showed the typical metallic-like behaviors for all Cr Ta films. The electron-phonon and electron-defect interactions were investigated, and correlated with variations of the film's composition and structure. • Cr Ta thin films are produced by GLAD co-sputtering. • Column tilt angle and composition can be tuned playing with Cr and Ta target currents. • Between 7 and 300 K, resistivity vs. temperature exhibit a metallic-like behaviors. • A crossover temperature is defined due to electron-phonon-defect interactions. • The crossover temperature is connected to composition and Debye temperature of Cr and Ta.