Experimental study demonstrates enhanced permittivity and temperature stability in barium titanate ceramics with barium zirconate doping, suggesting improved multilayer ceramic capacitor reliability.
The effects of BaZrO₃ addition on the structural and electrical properties of BaTiO₃-based base-metal-electrode (BME) multilayer ceramic capacitor (MLCC) ceramics were investigated. Dielectric compositions containing 0–9 wt% BaZrO₃ were fabricated using a conventional MLCC process, and their crystal structure, dielectric behavior, temperature stability, frequency stability, and insulation resistance were evaluated. X-ray diffraction and Rietveld refinement confirmed the formation of a single-phase perovskite structure for all compositions. Increasing BaZrO₃ content resulted in a systematic shift of diffraction peaks toward lower angles and an increase in unit-cell volume from 64.61 to 66.05 ų, indicating successful Zr incorporation into the BaTiO₃ lattice. The dielectric permittivity increased with BaZrO₃ addition and reached a maximum value of approximately 2,110 at 6 wt%, while dielectric loss decreased significantly. Capacitance stability against temperature and frequency variations was markedly improved with increasing BaZrO₃ content. In addition, insulation resistance increased substantially over the investigated temperature range, demonstrating enhanced electrical reliability.
No takes yet. Share an insight, caveat, or question.
Lee et al. (2026) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: