Annealing temperature dependence of Ohmic contact resistance and morphology on InAlN/GaN high electron mobility transistor structures

This is the authors' abstract. We don't add key points for this paper.

Ti/Al/Ni/Au Ohmic contact metallization on InAlN/GaN heterostructures both with and without a thin GaN cap layer was annealed at different temperatures. The minimum transfer resistance for the contacts of 0.65 Ω mm (specific contact resistivity of 2×10−5 Ω cm2) was achieved after 800 °C annealing for structures without the GaN cap, while those with the cap exhibited their lowest resistance at higher temperatures. The contact morphology showed considerable roughening by 750 °C but the carrier mobility was stable until annealing temperatures of 850 °C. Diffuse scattering experiments showed that the morphological roughness of the InAlN/GaN interface increased as a result of annealing at these temperatures and the data were consistent with outdiffusion of Ga into the InAlN. Unpassivated high electron mobility transistors with a gate dimension of 0.7×180 μm2 were fabricated using these contacts and showed a maximum drain current of 1.3 A/mm and an extrinsic transconductance of 366 mS/mm. The presence of the GaN cap increased the effective barrier height of Ni/Au Schottky contacts from 0.91 to 1.01 eV on the heterostructure.