Correlation between the fracture toughness and β‐crystal fraction in a β‐nucleated propylene‐based propylene–ethylene random copolymer

Propylene‐based propylene–ethylene random copolymer (PPR) has been widely used in the production of hot‐water pipes. To further improve its toughness and thermal resistance, β‐nucleating agents (β‐NAs) are frequently incorporated. In this study, PPR containing 5.6 mol % ethylene units was modified by two kinds of β‐NAs, that is, calcium pimelate andN,N′‐dicyclohexylterephthalamide. The notched Izod impact strength of PPR increased with the addition of the β‐NAs. Drastically different toughening effects were found between the two β‐NAs. The structure of PPR with and without a β‐NA was investigated by calorimetry, X‐ray diffraction, and thermomechanical analysis. The results indicated that the relative fraction of β crystals (kβ) in the injection‐molded specimens was determined by the type and content of β‐NA. The relationship betweenkβand the impact toughness was summarized. A critical value forkβ(0.68) was identified for the brittle–ductile transition of PPR. PPR with β‐NA having akβgreater than 0.68 displayed a higher impact strength than the other mixtures.