Nitrogen doped MgxZn1−xO/ZnO single heterostructure ultraviolet light-emitting diodes on ZnO substrates

We have grown nitrogen-doped MgxZn1−xO:N films on Zn-polar ZnO single crystal substrates by molecular beam epitaxy. As N-sources, we employed NO-plasma or NH3 gas itself. As x increased, optimum growth temperature window for smooth film morphology shifted to higher temperatures, while maintaining high N-concentration (∼1×1019 cm−3). The heterosructures of MgxZn1−xO:N (0.1≤x≤0.4)/ZnO were fabricated into light emitting diodes of 500-μm-diameter. We observed ultraviolet near-band-edge emission (λ∼382 nm) with an output power of 0.1 μW for a NO-plasma-doped LED and 70 μW for a NH3-doped one at a bias current of 30 mA.