Characterization of eva-based adhesives containing different amounts of rosin ester or polyterpene tackifier

Different amounts (50-170 php--parts per hundred parts of EVA, 33-63 wt%) of two tackifiers (hydrogenated rosin ester, polyterpene resin) were added to an ethylene vinyl acetate (EVA) copolymer containing 28 wt% vinyl acetate. The EVA and the tackifier were characterized using infrared (IR) spectroscopy, DSC measurements, and stress-controlled plate-plate rheology. The properties and compatibility of the EVA-tackifier mixtures were studied using DSC, DMTA, and stress-controlled plate-plate rheology. Immediate adhesion was measured as a quantification of tack, and the T-peel strength of roughened styrene-butadiene rubber/EVA-tackifier adhesive joints was also obtained. The increase in the amount of tackifier noticeably changed the crystallinity of polyethylene blocks in the EVA, and the temperature at the cross-over between the curves of the storage and loss moduli as a function of the temperature was displaced to a lower value. Whereas the hydrogenated rosin ester was compatible with the amorphous ethylene vinyl acetate copolymer regions of the EVA (Tg value increased) reducing its crystallinity, the polyterpene resin was compatible with the polyethylene blocks of the EVA (T g value was not modified), increasing its crystallinity. Immediate adhesion of the EVA-tackifier mixtures was improved by adding both hydrogenated rosin ester and polyterpene tackifiers. On the other hand, there was an optimum tackifier content at which the maximum T-peel strength value was obtained.