Preparation of high damping elastomer with broad temperature and frequency ranges based on ternary rubber blends

Based on the blends of chlorinated butyl rubber (CIIR), nitrile butadiene rubber (NBR) and chloroprene rubber (CR), a kind of high damping elastomer with broad temperature and frequency ranges is prepared. CIIR/NBR binary blend is prepared to take advantage of the immiscibility and the large difference in cross‐link density of the different phases caused by the curatives and accelerators migration. The dynamic mechanical analysis reveals that the binary blend was immiscible and its loss factor (tanδ) versus temperature curves show two separated and expanded loss peaks when compared with those of pure cured CIIR and NBR. In order to improve its damping properties at room temperature, the third component CR with the polarity between CIIR and NBR was blended into the binary blend. The resulted CIIR/NBR/CR ternary blend has gained effective damping properties (tanδ > 0.3) in the temperature range of −86.4 to 74.6°C and the frequency range of 10−2 to more than 109 Hz. Other effects on the damping properties of the ternary rubber were also studied.