Short-wave infrared barriode detectors using InGaAsSb absorption material lattice matched to GaSb

Short-wave infrared barriode detectors were grown by molecular beam epitaxy. An absorption layer composition of In0.28Ga0.72As0.25Sb0.75 allowed for lattice matching to GaSb and cut-off wavelengths of 2.9 μm at 250 K and 3.0 μm at room temperature. Arrhenius plots of the dark current density showed diffusion limited dark currents approaching those expected for optimized HgCdTe-based detectors. Specific detectivity figures of around 7×1010 Jones and 1×1010 Jones were calculated, for 240 K and room temperature, respectively. Significantly, these devices could support focal plane arrays working at higher operating temperatures.