Aluminum-doped n-type ZnTe layers grown by molecular-beam epitaxy

This is the authors' abstract. We don't add key points for this paper.

N-type ZnTe layers with high electron concentration are grown by molecular-beam epitaxy using aluminum as the donor species. The ZnTe:Al layers show a high structural quality with a narrow x-ray diffraction linewidth (24 arcsec) and a high carrier concentration up to n=4×1018 cm−3 with low resistivity (ρ=0.017 Ω cm). The dependence of the electron mobility on the carrier concentration suggests that the dominant scattering mechanisms in the ZnTe:Al layers are ionized impurity scattering and polar optical phonon scattering. The photoluminescence spectrum of moderately doped ZnTe layers shows strong Al–donor-related bound exciton lines: I2 (2.378 eV) and donor–acceptor pair emission (zero phonon energy=2.324 eV) with a weak deep-level emission (2.19 eV). Highly Al-doped layers show an increase in the deep-level emission intensity and a decrease in carrier mobility, which are interpreted in terms of the increase in the carrier compensation.