We have successfully fabricated 1.3-/spl mu/m AlGaInAs strain-compensated multiple-quantum-well (MQW) buried-heterostructure (BH) lasers by narrow-stripe selective metalorganic vapor-phase epitaxy. Based on the optimization of AlGaInAs strain compensated MQW and the Al-oxidation-free BH process, we obtained a low-threshold current of 12.5 mA and a relaxation frequency of more than 10 GHz at 85/spl deg/C for Fabry-Perot lasers. For distributed feedback lasers, we demonstrated a 10-Gb/s operation and transmission of over 16 Km for a single mode fiber at 100/spl deg/C. Furthermore, a record-low 25.8-mA/sub p-p/ modulation current for a 10-Gb/s modulation at 100/spl deg/C was demonstrated with shorter cavity and high grating-coupling coefficient. A median life of more than 1/spl times/10/sup 5/ h at 85/spl deg/C was estimated after an aging test of over 5000 h for these lasers. These superior characteristics at high temperatures were achieved by the combination of the high differential gain of AlGaInAs strain compensated MQW and the BH structure.
No takes yet. Share an insight, caveat, or question.
Nakamura et al. (2005) studied this question.
Synapse has enriched 3 closely related papers on similar clinical questions. Consider them for comparative context: