Electrical and structural characteristics of lanthanum-doped barium titanate ceramics

Single phase La-doped BaTiO3 with the formula Ba1−xLaxTi1−x/4O3: 0⩽x⩽0.20 was prepared by solid state reaction of oxide mixtures at 1350 °C, 3 days, in O2. The tetragonal distortion in undoped BaTiO3 decreased with x and samples were cubic for x⩾0.05. Both the tetragonal/cubic and orthorhombic/tetragonal transition temperatures decreased with x, but at different rates, and appeared to coalesce at x∼0.08. The value of the permittivity maximum at the tetragonal/cubic phase transition in ceramic samples increased from ∼10 000 for x=0 at 130 °C to ∼25 000 for x=0.06 at ∼−9 °C. At larger x, the permittivity maximum broadened, showed “relaxor”-type frequency dependent permittivity characteristics and continued to move to lower temperatures. Samples fired in O2 were insulating and showed no signs of donor doping whereas air-fired samples were semiconducting, attributable to oxygen loss.