Formation of quasicrystals in bulk glass forming Zr–Cu–Ni–Al alloys

Zr65Cu17.5Ni10Al7.5 as well as Zr69.5Cu12Ni11Al7.5 belong to the best glass forming alloys known. Glass transition temperatures of melt-spun ribbons are 372 and 360 °C, respectively. TEM and x-ray analysis of samples annealed above the glass transition temperature exhibit the formation of quasicrystalline microstructures with small amounts of crystalline phases. The metastable icosahedral phase is primitive with a quasilattice constant a=0.253 nm; its composition as determined by EDX is close to Zr69.5Cu12Ni11Al7.5. In both glasses, growth of the quasicrystals has been observed to be time-dependent (r∝t1/2), thus indicating a diffusion controlled transformation.